Mullite Bricks are a kind of high alumina refractory materials with mullite (3Al2O3·2SiO2) as the main crystal phase and containing 65~75% alumina content. Mullite Brick is widely used in blast furnace, hot blast stove and glass melting furnace with its various excellent properties of high temperature resistance, good thermal shock resistacne, high thermal conductivity and so on.
Mullite Refractory Bricks
Mullite Refractory Bricks are manufactured with mullite as the main raw material through molding and firing in the high temperature. Its refractoriness is higher up to 1790℃, its apparent initial softening temperature is 1600~1700℃. Its cold crushing strength is 70~260MPa. It has good thermal shock resistance.
Mullite Bricks Properties
- High refractoriness
- Good thermal shock resistance
- Strong acid erosion resistance
- High high-temperature strength
- Great wear resistance
- Low thermal expansion coefficient
- High thermal conductivity
Mullite Bricks Application
- Furnace roof of hot blast stove
- Furnace stack and bottom of blast furnace
- Regenerative chamber of glass melting furnace
- Ceramic high temperature furnace
Mullite Refractory Bricks Classification
There are two types of Sintered Mullite Brick and Fused Cast Mullite Brick
- Sintered Mullite Brick is made of bauxite chamotte as the main raw material by adding little clay or raw bauxite as the binding agent through molding and firing.
- Fused Cast Mullite Brick is produced with high bauxite, commercial alumina and fireclay as the raw materials by adding wood carbon or coke particle as the reducing agent after molding with electric melting method.
Fused Cast Mullite Brick’s Crystal is bigger than Sintered Mullite Brick’s, thermal shock resistance is better than Sintered Mullite Brick’s. Their high temperature properties depend on the distribution evenness of aluminium oxide content and mullite phase with glass.
Best Mullite Refractory Bricks In Rongsheng
Corundum Mullite Brick
Corundum Mullite Brick is made of white corundum, fused mullite and sintering aids as the raw materials through homogenizing, molding and high temperature firing. Corundum Mullite Brick is widely used for all kinds of high temperature furnaces linings and thermal insulation layers with features of high temperature resistance, low thermal conductivity, high strength and high thermal shock resistance.
Corundum Mullite Bricks Specifications
|Cold Crushing Strength||MPa||≥15||≥20|
|Linear Change On Reheating 1600℃*3h||%||≤0.2||≤0.2|
|Thermal Conductivity (hot-face 1000℃)||W/m*K||≤0.6||≤1.0|
|Thermal Shock Resistance (air-cold 1000℃)||Times||≥50||≥50|
|Maximum Service Temperature||℃||1600||1700~1750|
Lightweight Mullite Brick
Features of Lightweight Mullite Brick
- Low thermal conductivity, low thermal capacity
- High purity, low impurity content
- High temperature resistance, can directly contact with fire
- High strength, with good thermal shock resistance
|Sintered Mullite Brick Specifications|
|Bulk Density g/cm3||1.3~1.5||1.4~1.7||1.6~1.8|
|Cold Crushing Strength MPa||≥8||≥8||≥10|
|Apparent Initial Softening Temperature ℃ (0.1MPa, 0.6%)||≥1500||≥1500||≥1600|
|Linear Change On Reheating (1600℃*3h)||±0.5||±0.5||±0.3|
|Thermal Conductivity w/(m*k)
(Average temperature 800℃)
|Maximum Service Temperature ℃||1500||1550||1600|
Application of Lightweight Mullite Brick
Lightweight Mullite Brick applies to all kinds of industry furnace hot-face lined and backing lining in metallurgical industry, petrochemical industry, building materials industry, ceramic industry, and mechanical industry. Such as cracking furnace, conversion furnace, heating equipment, refine equipment, regeneration device, hot blast stove, soaking pit furnace, heat treatment furnace, resistance furnace, tunnel kiln, roller kiln, bell kiln and glass melting furnace and etc.
Regular Specification of Lightweight Mullite Brick is 230*114*65mm
Advantages of Lightweight Mullite Bricks Application In Kiln
Mullite Refractory Bricks Products have low thermal expansivity, high thermal conductivity, good thermal shock resistance, high high-temperature strength. They can resist in high temperature for long term without soften. They can resist any acid erosion, but they cannot service in the oxidizing atmosphere.
Mullite Bricks Manufacturers
Rongsheng, as one of the professional Mullite Bricks Manufacturers, Owns 2 factories for the refractory materials produce. RS has always insist on manufacturing high quality Mullite Refractory Bricks such as sintered mullite bricks, fused cast mullite bricks, corundum mullite bricks, lightweight mullite bricks, Zirconia Mullite Bricks etc. Contact Us for More Information! We will give you back as soon as possible.